MICA
panneau de mica
PROCESSUS DE FABRICATION OFFERTS
DÉCOUPE ET GRAVURE CNC
DÉCOUPE ET GRAVURE AU LASER
Properties | Value |
|---|---|
Advertised Thickness | 0.125" |
Gauge | N/A |
Thickness tolerance positive | 0.007" |
Thickness tolerance negative | 0.006" |
Top/Bottom Finish | Textured top side, smooth bottom |
Sourced from | Canada |
Détails généraux
Properties 2 | Value2 |
|---|---|
Cutting process | CNC Router |
Cut tolerance +/- | 0.005" |
Flatness tolerance before cutting | +/- 0.030" per foot |
Min part size | 1" x 2" |
Max part size | 44" x 30" |
Min hole size | 0.125" |
Min bridge size | 0.125" |
Min hole to edge distance | 0.38" |
Tab and slot Tolerance | 0.015" |
Spécifications de découpe du routeur CNC
Countersink Specs | Values3 |
|---|---|
Min countersink part size | 1" x 4" |
Max countersink part size | 14" x 46" |
Countersink Min Minor | 0.130" |
Countersink Max Major | 0.472" |
Countersink Min Hole Center to Material Edge | 0.361" |
Tapping Specs | Value4 |
|---|---|
Largest Tap | M10 x 1.5 |
Smallest Tap | M4 x 0.7 |
Min Flat Part Size Tapping | 0.949" x 1.5" |
Max Flat Part Size Tapping | 36" x 46" |
Tapping Min Hole to Edge | 0.063" |
Tapping Min Hole Center to Material Edge | Tap hole size/2 +0.063" |
Spécifications de taraudage
ABS Properties | Value5 |
|---|---|
Material Composition | Acrylonitrile Butadiene Styrene
|
Density | 65.664 lb/ft^3 |
Heat treatment process | N/A |
ASTM | D4673 |
Tensile Strength (Ultimate) | 4.5 ksi |
Tensile Strength (Yield) | 3.5 ksi |
Shear Strength | 2 ksi |
Shear Modulus | 75 ksi |
Fatigue Strength | 2 ksi |
Izod Impact Strength | 6.3 ft-lbs/in |
Coefficient of Friction | 0.19 – 0.21 |
Rockwell | R 90 - R100 |
Elongation at Break | 25% |
Elastic Modulus | 340 ksi |
Poisson’s Ratio | .35 |
Thermal Conductivity | 0.22 BTU/h-ft °F |
Vicat Softening Temp | 150 °F |
Melting Point | 390 °F |
Magnetic | No |
Does it Rust | No |
Propriétés de l'ABS
Spécifications de la fraise conique
CARACTÉRISTIQUES
Ce matériau stratifié pressé à chaud est composé de plusieurs couches de papier phlogopite liées entre elles par de la colle silicone ou de la résine époxy pour former une feuille plate
Stabilité thermique élevée
Stabilité dimensionnelle élevée
Retardateur de flamme à haute température
Excellente isolation électrique haute tension
Résistance à l'abrasion
INCONVÉNIENTS
Fragile et sujet aux fissures
APPLICATIONS PRODUITS ET INDUSTRIELS
appareils électroménagers, meubles